50

AKSAD GROUP PETROCHEM

ABS-50


 

Application

Electronic and Electrical parts, vacuum cleaner, washing machine cover and Refrigerator door cap & etc

Classification

General purpose

Characteristic

Medium Impact, High rigidity

 

Property

Test method

Test condition

Unit

Typical value

ABS-50 specificatio

Izod impact

D-256

6.4 mm , notched

Kj/m²

23

Min19

Melt flow index

D-1238

220ºc , 10 kg

gr/10 min

35

29-39

Rock well hardness

D-785

........

R-scale

109

95-115

HDT

D-648

1.82 m pa

ºc

85

Min82

Vicat softening Temp

D-1525

5kg/50°c

ºc

95

Min 93

Tensile strength

D-638

23ºc , 50 mm/min

Kg/cm²

455

Min420

Tensile elongation

D-638

23ºc , 50 mm/min

%

20

Min 16

Flexural strength

D-790

23ºc , 2.8 mm/min

Kg/cm²

650

Min 620

Flexural Modulus

D-790

23ºc , 2.8 mm/min

Kg/cm²

22000

Min17000

Specific Gravity

D-792

23ºc

..

1.04

1.04

Molding Shrinkage

D-955

%

0.4-0.7

0.4-0.7

Flammability

Ul94

1/8inch(3.2mm)

..

HB

HB

 

TYPICAL ABS PROCESSING CONDITIONS

DRYING:

it is recommended that GBPC ABS Resins be dried at (80-85°c)for 3 hours.

The following molding conditions are recommended starting point for GBPC ABS Resin. A moisture level of ≤0.1% should be reached before injection molding the resin.

Some modifications may be required depending on the specific molding equipment and part configuration

INJECTION MOLDIN

Rear Temp(°c)

Center Temp (°c)

Center Temp (°c)

Front Temp (°c)

Nozzle Temp (°c)

Melt Temp

(°c)

190-200

200-210

210-220

210-220

215-225

230


 

 

 